论文部分内容阅读
摘 要：针对我国室内装修材料环保性能差的问题，提出一种新型室内装修环保材料的制备，更符合节能环保的发展方向。由于装饰砂浆在近年来受到人们的高度关注，其装饰效果也获得提高，逐渐在装修行业站住脚跟。因此，文章基于装饰砂浆研究制备室内环保装饰砂浆，并通过相关性能测试检验其是否符合国家相关标准。
关键词：装饰砂浆;性能測试;视觉效果
中图分类号：TU521.1 文献标识码：A 文章编号：1001-5922（2021）10-0123-04
Preparation of Environmental Protection Materials for Interior Decoration and Its Application in Visual Communication
Yu Lei
（Shaanxi Youth Vocational College， Xi an 710068， China ）
Abstract：Aiming at the problem of poor environmental protection performance of indoor decoration materials in my country， a new type of preparation of environmental protection materials for indoor decoration is proposed， which is more in line with the development direction of energy saving and environmental protection. As decorative mortar has received great attention in recent years， its decorative effect has also been improved， and it has gradually gained a foothold in the decoration industry. Therefore， based on decorative mortar， this paper studies the preparation of indoor environmental protection decorative mortar， and tests whether it meets the relevant national standards through relevant performance tests.
Key words：decorative mortar; performance test; visual effect
由于人们生活水平的提高，人们对生活质量的要求有了进一步的提高，节能、环保等观念逐渐扎根在人们的思想中，因此人们更加注重自身居住、工作、娱乐等室内场所的环境质量。在环保观念的持续发展的情况下，室内环境的装饰在满足人们审美需求的同时，需严格遵守环保的原则，选用环保型装饰材料，以确保人们拥有绿色、健康的生存空间。因此，文章针对以上问题研究制备了一种新型室内环保装饰砂浆，该砂浆采用纯天然原材料，低污染的生产模式，在保证室内装饰美观的同时，满足装饰材料绿色环保的理念，使人们在健康的空间和环境中生存。
1 材料与方法
1.1 试验原材料
本试验主要试剂为：水泥（山东问渠新材料科技有限公司，P.O 32.5R）;石灰石（广西浙创化工有限公司，粒径10～100目）;海泡石（东风海泡石有限责任公司，工业级）;硅藻土（吉林省长白山地区生产，工业级）;纤维素醚（成都市山马生物科技有限公司，工业级）;可再分散乳胶粉（德国瓦克化学公司，工业级）;短切聚丙烯纤维（深圳市亚泰达科技有限公司，工业级）;木质素磺酸盐（重庆博瑞达建材公司，工业级）。
1.2 试验仪器
电子天平（梅特勒-托利多仪器（上海）有限公司，Ml-203）;水泥净桨搅拌机（无锡建仪仪器机械有限公司 ，NJ-160A）;初期干燥抗干裂试验仪（中斯特朗天津测控技术有限公司，BGD 597） ;智能粘结强度检测仪（沧州博伟试验仪器有限公司，HC-6000C）。抗压抗折强度一体机（山东万辰试验机有限公司，WT）。
1.3 环保装饰砂浆的制备
环保装饰砂浆的制备工艺包括干粉混合和加水混合搅拌两道程序。干粉混合是将贝壳粉、白水泥、海泡石、硅藻土、乳胶粉、淀粉醚、纤维素醚、粉末消泡剂以及减水剂放入搅拌锅中均匀搅拌，使其充分混合;然后平缓的将水加入搅拌锅中，开启低速搅拌模式，搅拌时间为15s，利用抹刀将搅拌叶刮干净，再将搅拌叶安装完整，以此程序再次进行75s的搅拌，加水量需考虑砂浆所需稠度。完成砂浆制备后，放置备用。
1.4 性能测试
1.4.1 一般性能测试
（1）可操作时间的测定。将制备好的砂浆静置30min，制备尺寸为400mm×400mm×40mm的混凝土板上。将静置好的砂浆均匀涂抹于混凝土板上，混泥土板与抹刀移动角度的两边夹角度数为90°和60°，以该模式进行持续刮涂，若操作顺利，30min可完成该操作。
（2）初期的干燥抗裂性能测试。将制备好的砂浆涂抹在石棉板表面，将其刮平为厚度为3mm的砂浆石棉板，并将其放置在室内直至表面干燥，而后将砂浆石棉板放置在初期干燥抗开裂试验仪器中。待6h后取出，在半米范围内用肉眼观察其表面是否开裂。
（3）拉伸粘结强度测试。测定砂的拉伸粘结强度。具体步骤为：提前准备粘结强度成型模具。该模具有10个孔，每孔规格皆为50mm×50mm×5mm。将制备出的试件放置在需相对湿度在50%左右、温度在23℃左右的环境中养护一个月。待养护完成后，将拉伸粘结度实验仪的拉伸粘结头和试件用AB胶进行粘结，而后放回原位继续养护一整天。最后的结果若大于0.5MPa，那么其拉伸粘结强度满足国家标准。 （4）吸水量测试。利用规格为40mm×40mm×160mm的三联试模具制备试件，将砂浆倒入模具后放入标准养护箱内养护5d后取出进行脱模，而后进行二次养护，此次养护时间为16d。待16d后利用密封料密封试件，标准养护7d。测定试件质量，数值精确到小数点后两位。而后将试件直立在有水的平底盘中，确保试件没入水的高度在0.5～1.0cm。30min后取出试件，并用湿润的布将试件上的水分擦拭干净后，再次测量其质量，并在6h后重复该操作。
吸水量的计算公式如下：
式（1）中Wdt为吸水量，单位g;mt为没入水后的试件质量，单位g;md为初始质量，单位g。
计算出6次实验所得吸水值的平均数，数值精确到小数点后一位。
1.4.2 力学性能测试
依据GB/T 17671-1999标准检测装饰砂浆的抗压抗折强度。通过调整胶砂比对砂浆的力学性能和物理性质进行测试。砂浆比分别为1∶1.0，1∶1.33，1∶1.67。按比例调配好砂浆后，制备成尺寸为40mm×40mm×160mm的试件。标准养护至指定龄期后，置于WT型抗压抗折一体机中测定试件的力学性能。并对结果进行统计。
1.4.3 进化甲醛性能测试
依据JC/T1074-2008标准，测试装饰砂浆的吸附甲醛性能。由于室内装饰砂浆在国家标准中为I类材料，因此其净化效果和甲醛净化率都应参考I类材料进行判定。具体测试步骤为：首先选择两个尺寸为1250mm×800mm×1000mm的玻璃实验舱A和B，A舱为样品舱，B舱为空白舱。运用橡胶将实验舱侧壁的采集气体专用口紧塞，在另一侧壁安装风扇使舱内空气更加均匀。具体步骤为：按标准将养护后的砂浆涂板和空白玻璃板置于A、B两舱，在放置时，注意放置方向为砂浆板有砂浆的一面面向舱中心;将玻璃平皿置于采集气体口底部，让注射器注射到玻璃平皿后立刻封闭A、B两舱;将采集气体专用口打开后，运用微量注射器将（3±0.25）μl分析纯的甲醛溶液注射至玻璃平皿后立刻塞紧橡胶塞;封闭1h后开启电风扇，使其处于开启状态30min后采集舱内气体，测定收集气体中甲醛的浓度，记为n0。1d后再次测定其浓度，该浓度则为终止浓度，表示为n1。
1.4.4 装饰砂浆的吸放湿性能测试
依据GB/T 20312—2006标准对装饰砂浆的吸放湿性能进行检测。采用干燥器法对制备的装饰砂浆的吸放湿性能进行检测。將搅拌好的砂浆依照要求涂膜板上，并实施养护工作。养护完成后，将其放入环境湿度合适的干燥器中，所配置的盐溶液决定了其环境湿度。盐溶液吸放湿性能测试设备如图3所示。
将质量为15g的贝壳粉、硅藻土以及海泡石分别放入培养皿中，并放入60℃干燥箱中进行烘干，90min后取出。取出后重新称取其质量，各材料均保留10g进行试验。
将相对湿度75%的NaCl饱和溶液放置于干燥器底部;将贝壳粉、硅藻土以及海泡石培养皿放入干燥器内并将盖上干燥器盖;并将干燥器放置于环境温度保持在25℃养护箱内;每隔10min取出进行称重并记录，直至其处于饱和吸湿状态，即质量不再增加。
将相对湿度33%的MgCl2·H2O混合溶液放置于干燥器底部;将贝壳粉、硅藻土和海泡石培养皿放入干燥器内并盖上干燥器盖;将干燥器放入环境温度为25℃的养护箱内;每隔10min取出进行称重并记录，直至其处于完全放湿状态，即质量不再增加。
2 结果与讨论
2.1 室内环保装饰砂浆的一般性能测试结果
室内环保装饰砂浆的一般性能测试如表1所示。
从表1中可证明本试验多制备的室内环保装饰砂浆性能满足《墙体饰面砂浆》的标准要求。
2.2 力学性能测试结果
装饰砂浆的力学测试结果如表2所示。
2.3 甲醛性能测试结果
图4为3种不同胶砂比砂浆甲醛净化率。从图4中看出，标号1配比砂浆的甲醛净化率最低，为71%;标号2、标号3配比砂浆的甲醛净化率不相上下，分别为77%和79%。因此标号2、标号3配比砂浆的甲醛净化率更好。
2.4 吸放湿测试结果
吸湿率、放湿率计算公式如式（1）、式（2）所示：
经计算，得出不同时间下吸湿率与放湿率的变化曲线。具体如图5、图6所示。
2.5 室内环保装饰砂浆效果
通过对室内环保装饰砂浆的研究和制备，能够获得色彩明亮、颜色鲜艳的装饰效果，具体视觉效果图如图7所示。
3 结论
文章对室内装修环保材料的制备方式进行了研究，并开展了性能测试，得出以下结论：
（1）室内环保装饰砂浆的制备工艺可分为两道工艺：干粉混合和加水混合搅拌。先进行干粉混合，然后加水混合。
（2）在对装饰砂粉时间进行测试时，需依照相关标准和要求，例如测试砂浆的抗压抗折强度时需按照《水泥胶砂强度检验方法（ISO法）》的相关要求进行测试。
（3）室内环保装饰砂浆在30min内的吸水量为1.5g，240h内砂浆吸水量为4.7g;砂浆干燥抗裂测试未见裂纹;粘结强度达到0.9MPa。因此该砂浆满足JC/ T 1024—2007《墙体饰面砂浆》中相关标准要求。
综上，本试验制备的室内环保装饰砂浆满足国家相关标准要求，获得了颜色明亮鲜艳、视觉效果极佳的装饰砂浆。
参考文献
[1]肖力光，丁艳波.秸秆碱活化预处理对秸秆板性能影响的研究[J].新型建筑材料，2021，48（06）：124-126+135.
[2]黄朝广.水性聚氨酯涂料在建筑领域应用的研究进展[J].合成材料老化与应用，2021，50（02）：143-146.
[3]贾舒婷.早强木纹装饰砂浆板的制备与性能研究[J].新型建筑材料，2019，46（06）：76-78+98.
[4]盖广清，杨崇尚.贝壳粉/海泡石/硅藻土混合掺料对室内装饰砂浆性能的影响[J].吉林建筑大学学报，2019，36（02）：57-60+66.
[5]董浩，罗杰，张振升，等.“水泥+矿物掺和料”组合胶凝体系对水泥砂浆性能的影响[J].长江工程职业技术学院学报，2020，37（04）：18-22.
[6]许浩锋，翟灵杰，胡凯，等.纤维改性硫氧镁基仿木保温材料性能研究[J].宁波大学学报（理工版），2020，33（02）：60-65.
[7]王红霞，王星.复合改性剂对干混砂浆物理力学性能的影响[J].山西建筑，2020，46（05）：1-3.
[8]裴须强，朱玉雪，张帅.丙烯酸乳液改性水泥加固砂浆的性能研究[J].硅酸盐通报，2020，39（02）：409-415.
[9]谢永刚.环氧树脂砂浆在水利工程上的应用[J].粘接，2019，40（11）：24-28.
[10]张婵韬，段政彬.可分散性乳胶粉对玻化微珠保温砂浆干湿循环下损伤影响研究[J].混凝土世界，2020（02）：63-67.
关键词：装饰砂浆;性能測试;视觉效果
中图分类号：TU521.1 文献标识码：A 文章编号：1001-5922（2021）10-0123-04
Preparation of Environmental Protection Materials for Interior Decoration and Its Application in Visual Communication
Yu Lei
（Shaanxi Youth Vocational College， Xi an 710068， China ）
Abstract：Aiming at the problem of poor environmental protection performance of indoor decoration materials in my country， a new type of preparation of environmental protection materials for indoor decoration is proposed， which is more in line with the development direction of energy saving and environmental protection. As decorative mortar has received great attention in recent years， its decorative effect has also been improved， and it has gradually gained a foothold in the decoration industry. Therefore， based on decorative mortar， this paper studies the preparation of indoor environmental protection decorative mortar， and tests whether it meets the relevant national standards through relevant performance tests.
Key words：decorative mortar; performance test; visual effect
由于人们生活水平的提高，人们对生活质量的要求有了进一步的提高，节能、环保等观念逐渐扎根在人们的思想中，因此人们更加注重自身居住、工作、娱乐等室内场所的环境质量。在环保观念的持续发展的情况下，室内环境的装饰在满足人们审美需求的同时，需严格遵守环保的原则，选用环保型装饰材料，以确保人们拥有绿色、健康的生存空间。因此，文章针对以上问题研究制备了一种新型室内环保装饰砂浆，该砂浆采用纯天然原材料，低污染的生产模式，在保证室内装饰美观的同时，满足装饰材料绿色环保的理念，使人们在健康的空间和环境中生存。
1 材料与方法
1.1 试验原材料
本试验主要试剂为：水泥（山东问渠新材料科技有限公司，P.O 32.5R）;石灰石（广西浙创化工有限公司，粒径10～100目）;海泡石（东风海泡石有限责任公司，工业级）;硅藻土（吉林省长白山地区生产，工业级）;纤维素醚（成都市山马生物科技有限公司，工业级）;可再分散乳胶粉（德国瓦克化学公司，工业级）;短切聚丙烯纤维（深圳市亚泰达科技有限公司，工业级）;木质素磺酸盐（重庆博瑞达建材公司，工业级）。
1.2 试验仪器
电子天平（梅特勒-托利多仪器（上海）有限公司，Ml-203）;水泥净桨搅拌机（无锡建仪仪器机械有限公司 ，NJ-160A）;初期干燥抗干裂试验仪（中斯特朗天津测控技术有限公司，BGD 597） ;智能粘结强度检测仪（沧州博伟试验仪器有限公司，HC-6000C）。抗压抗折强度一体机（山东万辰试验机有限公司，WT）。
1.3 环保装饰砂浆的制备
环保装饰砂浆的制备工艺包括干粉混合和加水混合搅拌两道程序。干粉混合是将贝壳粉、白水泥、海泡石、硅藻土、乳胶粉、淀粉醚、纤维素醚、粉末消泡剂以及减水剂放入搅拌锅中均匀搅拌，使其充分混合;然后平缓的将水加入搅拌锅中，开启低速搅拌模式，搅拌时间为15s，利用抹刀将搅拌叶刮干净，再将搅拌叶安装完整，以此程序再次进行75s的搅拌，加水量需考虑砂浆所需稠度。完成砂浆制备后，放置备用。
1.4 性能测试
1.4.1 一般性能测试
（1）可操作时间的测定。将制备好的砂浆静置30min，制备尺寸为400mm×400mm×40mm的混凝土板上。将静置好的砂浆均匀涂抹于混凝土板上，混泥土板与抹刀移动角度的两边夹角度数为90°和60°，以该模式进行持续刮涂，若操作顺利，30min可完成该操作。
（2）初期的干燥抗裂性能测试。将制备好的砂浆涂抹在石棉板表面，将其刮平为厚度为3mm的砂浆石棉板，并将其放置在室内直至表面干燥，而后将砂浆石棉板放置在初期干燥抗开裂试验仪器中。待6h后取出，在半米范围内用肉眼观察其表面是否开裂。
（3）拉伸粘结强度测试。测定砂的拉伸粘结强度。具体步骤为：提前准备粘结强度成型模具。该模具有10个孔，每孔规格皆为50mm×50mm×5mm。将制备出的试件放置在需相对湿度在50%左右、温度在23℃左右的环境中养护一个月。待养护完成后，将拉伸粘结度实验仪的拉伸粘结头和试件用AB胶进行粘结，而后放回原位继续养护一整天。最后的结果若大于0.5MPa，那么其拉伸粘结强度满足国家标准。 （4）吸水量测试。利用规格为40mm×40mm×160mm的三联试模具制备试件，将砂浆倒入模具后放入标准养护箱内养护5d后取出进行脱模，而后进行二次养护，此次养护时间为16d。待16d后利用密封料密封试件，标准养护7d。测定试件质量，数值精确到小数点后两位。而后将试件直立在有水的平底盘中，确保试件没入水的高度在0.5～1.0cm。30min后取出试件，并用湿润的布将试件上的水分擦拭干净后，再次测量其质量，并在6h后重复该操作。
吸水量的计算公式如下：
式（1）中Wdt为吸水量，单位g;mt为没入水后的试件质量，单位g;md为初始质量，单位g。
计算出6次实验所得吸水值的平均数，数值精确到小数点后一位。
1.4.2 力学性能测试
依据GB/T 17671-1999标准检测装饰砂浆的抗压抗折强度。通过调整胶砂比对砂浆的力学性能和物理性质进行测试。砂浆比分别为1∶1.0，1∶1.33，1∶1.67。按比例调配好砂浆后，制备成尺寸为40mm×40mm×160mm的试件。标准养护至指定龄期后，置于WT型抗压抗折一体机中测定试件的力学性能。并对结果进行统计。
1.4.3 进化甲醛性能测试
依据JC/T1074-2008标准，测试装饰砂浆的吸附甲醛性能。由于室内装饰砂浆在国家标准中为I类材料，因此其净化效果和甲醛净化率都应参考I类材料进行判定。具体测试步骤为：首先选择两个尺寸为1250mm×800mm×1000mm的玻璃实验舱A和B，A舱为样品舱，B舱为空白舱。运用橡胶将实验舱侧壁的采集气体专用口紧塞，在另一侧壁安装风扇使舱内空气更加均匀。具体步骤为：按标准将养护后的砂浆涂板和空白玻璃板置于A、B两舱，在放置时，注意放置方向为砂浆板有砂浆的一面面向舱中心;将玻璃平皿置于采集气体口底部，让注射器注射到玻璃平皿后立刻封闭A、B两舱;将采集气体专用口打开后，运用微量注射器将（3±0.25）μl分析纯的甲醛溶液注射至玻璃平皿后立刻塞紧橡胶塞;封闭1h后开启电风扇，使其处于开启状态30min后采集舱内气体，测定收集气体中甲醛的浓度，记为n0。1d后再次测定其浓度，该浓度则为终止浓度，表示为n1。
1.4.4 装饰砂浆的吸放湿性能测试
依据GB/T 20312—2006标准对装饰砂浆的吸放湿性能进行检测。采用干燥器法对制备的装饰砂浆的吸放湿性能进行检测。將搅拌好的砂浆依照要求涂膜板上，并实施养护工作。养护完成后，将其放入环境湿度合适的干燥器中，所配置的盐溶液决定了其环境湿度。盐溶液吸放湿性能测试设备如图3所示。
将质量为15g的贝壳粉、硅藻土以及海泡石分别放入培养皿中，并放入60℃干燥箱中进行烘干，90min后取出。取出后重新称取其质量，各材料均保留10g进行试验。
将相对湿度75%的NaCl饱和溶液放置于干燥器底部;将贝壳粉、硅藻土以及海泡石培养皿放入干燥器内并将盖上干燥器盖;并将干燥器放置于环境温度保持在25℃养护箱内;每隔10min取出进行称重并记录，直至其处于饱和吸湿状态，即质量不再增加。
将相对湿度33%的MgCl2·H2O混合溶液放置于干燥器底部;将贝壳粉、硅藻土和海泡石培养皿放入干燥器内并盖上干燥器盖;将干燥器放入环境温度为25℃的养护箱内;每隔10min取出进行称重并记录，直至其处于完全放湿状态，即质量不再增加。
2 结果与讨论
2.1 室内环保装饰砂浆的一般性能测试结果
室内环保装饰砂浆的一般性能测试如表1所示。
从表1中可证明本试验多制备的室内环保装饰砂浆性能满足《墙体饰面砂浆》的标准要求。
2.2 力学性能测试结果
装饰砂浆的力学测试结果如表2所示。
2.3 甲醛性能测试结果
图4为3种不同胶砂比砂浆甲醛净化率。从图4中看出，标号1配比砂浆的甲醛净化率最低，为71%;标号2、标号3配比砂浆的甲醛净化率不相上下，分别为77%和79%。因此标号2、标号3配比砂浆的甲醛净化率更好。
2.4 吸放湿测试结果
吸湿率、放湿率计算公式如式（1）、式（2）所示：
经计算，得出不同时间下吸湿率与放湿率的变化曲线。具体如图5、图6所示。
2.5 室内环保装饰砂浆效果
通过对室内环保装饰砂浆的研究和制备，能够获得色彩明亮、颜色鲜艳的装饰效果，具体视觉效果图如图7所示。
3 结论
文章对室内装修环保材料的制备方式进行了研究，并开展了性能测试，得出以下结论：
（1）室内环保装饰砂浆的制备工艺可分为两道工艺：干粉混合和加水混合搅拌。先进行干粉混合，然后加水混合。
（2）在对装饰砂粉时间进行测试时，需依照相关标准和要求，例如测试砂浆的抗压抗折强度时需按照《水泥胶砂强度检验方法（ISO法）》的相关要求进行测试。
（3）室内环保装饰砂浆在30min内的吸水量为1.5g，240h内砂浆吸水量为4.7g;砂浆干燥抗裂测试未见裂纹;粘结强度达到0.9MPa。因此该砂浆满足JC/ T 1024—2007《墙体饰面砂浆》中相关标准要求。
综上，本试验制备的室内环保装饰砂浆满足国家相关标准要求，获得了颜色明亮鲜艳、视觉效果极佳的装饰砂浆。
参考文献
[1]肖力光，丁艳波.秸秆碱活化预处理对秸秆板性能影响的研究[J].新型建筑材料，2021，48（06）：124-126+135.
[2]黄朝广.水性聚氨酯涂料在建筑领域应用的研究进展[J].合成材料老化与应用，2021，50（02）：143-146.
[3]贾舒婷.早强木纹装饰砂浆板的制备与性能研究[J].新型建筑材料，2019，46（06）：76-78+98.
[4]盖广清，杨崇尚.贝壳粉/海泡石/硅藻土混合掺料对室内装饰砂浆性能的影响[J].吉林建筑大学学报，2019，36（02）：57-60+66.
[5]董浩，罗杰，张振升，等.“水泥+矿物掺和料”组合胶凝体系对水泥砂浆性能的影响[J].长江工程职业技术学院学报，2020，37（04）：18-22.
[6]许浩锋，翟灵杰，胡凯，等.纤维改性硫氧镁基仿木保温材料性能研究[J].宁波大学学报（理工版），2020，33（02）：60-65.
[7]王红霞，王星.复合改性剂对干混砂浆物理力学性能的影响[J].山西建筑，2020，46（05）：1-3.
[8]裴须强，朱玉雪，张帅.丙烯酸乳液改性水泥加固砂浆的性能研究[J].硅酸盐通报，2020，39（02）：409-415.
[9]谢永刚.环氧树脂砂浆在水利工程上的应用[J].粘接，2019，40（11）：24-28.
[10]张婵韬，段政彬.可分散性乳胶粉对玻化微珠保温砂浆干湿循环下损伤影响研究[J].混凝土世界，2020（02）：63-67.