纯钛VAR熔池形貌和凝固组织模拟及其工业验证

来源 :钢铁钒钛 | 被引量 : 0次 | 上传用户:chier00
下载到本地 , 更方便阅读
声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架
论文部分内容阅读
运用ANSYS和μMat Ic软件分析了980 mm纯钛锭VAR过程中熔池形貌以及凝固组织的变化规律。模拟计算结果表明:起弧阶段的熔池很小,呈浅U型;随后熔池形貌由U型逐渐变为V型;当坩埚内热量输入与输出达到平衡时,熔炼进入稳定阶段,熔池深度和宽度不再变化;补缩过程中,熔池不断缩小直至消失。凝固组织的变化规律为:与坩埚壁接触的钛液快速冷却形成细晶组织;随着熔炼的进行,以枝晶形状生长的部分细晶粒最终形成具有一定择优取向的柱状晶;铸锭中心区域和液固临界区域,晶粒直接在金属液内形核并长大,形成的等轴晶粒阻碍了柱状晶的生长,发生柱状晶-等轴转变。通过解剖工业铸锭验证,熔池形貌和凝固组织与数值模型的计算结果相吻合。 The morphology of molten pool and the variation of solidified structure in VAR process of 980 mm titanium ingot were analyzed by ANSYS and μMat Ic software. The simulation results show that the molten pool in the arc-striking phase is small and shallow U-shape, and then the shape of the molten pool is gradually changed from U-shape to V-shape. When the heat input and output in the crucible reach a balance, The depth and width of the pool no longer change; during the shrinking process, the pool continues to shrink until it disappears. The variation regularity of the solidified structure is that titanium liquid in contact with the crucible wall is rapidly cooled to form fine grain structure. As the smelting progresses, a part of fine grains growing in dendritic shape finally form a columnar crystal with a certain preferred orientation; In the region and the liquid-solid critical region, the grains nucleate and grow directly in the molten metal. The formation of equiaxed grains hinders the growth of columnar crystals and the columnar crystal-isometric transformation occurs. By anatomical industrial ingot verification, the shape of the weld pool and the solidified structure are consistent with the numerical results.
其他文献
在我国大西北,每逢红白喜事,总少不了一种乐器,可欢快喜庆,亦可哀婉凄凉,它就是唢呐.“唢呐一出,谁与争锋”,一声唢呐曲,尽显地方人文风俗特色.rn唢呐,双簧齐鸣乐器,在山东一
期刊
历史城市,特别是其中所蕴含的城市遗产,是全人类共同的财富,城市保护也因此受到全世界的广泛重视.但历史城市的保护不仅意味着巨额资金投入,其中的建筑遗产由于在能源利用效