在进行理论计算的基础上,对冶炼不锈钢的氩氧过程铬的挥发行为作了实验测定。测定结果表明,挥发物中的Fe/Cr比在1.1~2.2之间,而在现行的冶炼不锈钢工艺中,每炉铬的挥发量为金属铬总量的1.5~2.5%左右。
Based on the theoretical calculation, the volatilization behavior of chromium in argon-oxygen process of smelting stainless steel was experimentally determined. The results show that the Fe / Cr ratio in the volatiles is between 1.1 and 2.2. In the existing smelting stainless steel process, the amount of chromium volatilized per kiln is about 1.5 to 2.5% of the total amount of chromium metal.