【摘 要】
：
The surface mechanical attrition treatment (SMAT) technique was developed to synthesize a nanocrystalline (NC)layer on the surface of metallic materials for upg
【机 构】
：
State Key Laboratory of Nonlinear Mechanics,Shenyang National Laboratory for Materials Sciences,LASM
论文部分内容阅读
The surface mechanical attrition treatment (SMAT) technique was developed to synthesize a nanocrystalline (NC)layer on the surface of metallic materials for upgrading their overall properties and performance. In this paper, by means of SMAT to a pure zirconium plate at the room temperature, repetitive multidirectional peening of steel shots (composition (wt%): 1C, 1.5Cr, base Fe) severely deformed the surface layer. A NC surface layer consisting of the intermetallic compound FeCr was fabricated on the surface of the zirconium. The microstructure characterization of the surface layer was performed by using X-ray diffraction analysis, optical microscopy, scanning and transmission electron microscopy observations. The NC surface layer was about 25 μm thick and consisted of the intermetallic compound FeCr with an average grain size of 25+10 nm. The deformation-induced fast diffusion of Fe and Cr from the steel shots into Zr occurred during SMAT, leading to the formation of intermetallic compound. In addition, the NC surface layer exhibited an ultrahigh nanohardness of 10.2 GPa.
其他文献
药物性肝损害是抗结核治疗过程中常见的毒副作用,如治疗不当常导致化疗中断,直接影响到抗结核治疗能否顺利开展及患者的预后.近年来,我们采用自拟保肝解毒汤治疗抗结核药致药
This paper presents a study on effects of carburized parts on residual stresses of thin-rimmed spur gears with symmetric web arrangements due to the case-carbur
本文进行了钢筋混凝土梁在空气环境、淡水环境和盐水环境中的疲劳试验,研究了反复荷载下三种环境中梁的变形发展过程和疲劳寿命.结果表明,在环境和反复荷载的共同作用下,钢筋
The paper shows, how the quality of workpieces to be heat treated can be improved by using the technology of fixture-quenching. Different fixture systems, like
The aim of this investigation was the determination of the predominant wear mechanism on three-body abrasion of fully pearlitic low alloy steel. Furthermore, th
Plain carbon steels were dipped in molten aluminum bath at 720℃±5℃ and diffused for 1, 2.5 and 6 hours respectively and then boronized at 950℃ for 6 hours.
The appearance of lower hardness at the surface than at the core after through-hardening of steels is known as"inverse quench-hardening." Pioneering work was pe
Two hard, carbon-based solid lubricant coatings, Graphit-iCTM and Dymon-iCTM, have been developed that offer considerable benefits for industry. Both of these n
The compound bioceramic coating containing calcium (Ca) and phosphorus (P) on titanium alloy substrate was prepared by means of micro-arc oxidation (MAO) treatm
The transformation behavior of a 40Cr2Ni2MoV cast steel manufactured by electroslag remelting (ESR) has been investigated. Compared to a forged steel, the incub