WO3 x(x∶0～ 1)是一种优良的光、电、气致色变半导体材料。本研究通过在电化学腐蚀的钨丝针尖上原位加热生长了一系列的样品 ,发现了一种新奇的WO3 x结构 ,电子衍射和高分辨研究证明其是一种非常有序的晶体丝织构行为。图 1是生长WO3 x纳米棒特征的SEM图像 ,钨针尖上布满了
WO3 x (x: 0 ~ 1) is an excellent optical, electrical and gas-chromatic semiconducting material. In this study, a series of samples were grown by in-situ heating on electrochemically-corded tungsten tips and a novel WO3x structure was discovered. Electron diffraction and high-resolution studies have shown that it is a very ordered crystalline silk Constructive behavior. Figure 1 is an SEM image of the growth characteristics of WO3 x nanorods, covered with tungsten tips