The magnetocaloric properties of melt-spun La(Fe,Si)13 and MnFePGe compounds were investigated. Very large value of magnetic entropy change ｜ΔS｜=31 and 35.4 J·(kg·K)-1 under 5 T were obtained at 201 K in LaFe11.8Si1.2 melt-spun ribbons and at around 317 K in Mn1.1Fe0.9P0.76Ge0.24 melt-spun ribbons, respectively. The large magnetocaloric effect results from a more homogenous element distribution related to the very high cooling rate during melt-spinning. The excellent MCE properties, the low materials cost and the accelerated aging regime make the melt-spun-type La(Fe,Si)13 and MnFePGe materials an excellent candidate for magnetic refrigerant applications.
Very large value of magnetic entropy change | ΔS | = 31 and 35.4 J · (kg · K) -1 under 5 T were obtained at 201 K in LaFe11.8Si1.2 melt-spun ribbons and at around 317 K in Mn1.1Fe0.9P0.76Ge0.24 melt-spun ribbons, respectively. The large magnetocaloric effect results from a more homogenous element distribution related to the very high cooling The excellent MCE properties, the low material cost and the accelerated aging regime make the melt-spun-type La (Fe, Si) 13 and MnFePGe materials an excellent candidate for magnetic refrigerant applications.