Spherical icosahedral quasicrystalline phase (I-phase) was obtained by introducing Ca into Mg-Zn-Y alloy under conventional casting conditions. Due to the addit
【机 构】
：
School of Materials Science and Engineering
论文部分内容阅读
Spherical icosahedral quasicrystalline phase (I-phase) was obtained by introducing Ca into Mg-Zn-Y alloy under conventional casting conditions. Due to the addition of Ca, Mg45Zn50Y4.5Ca0.5 primary I-phase, which is thermodynamically stable and homogeneously distributed, was generated instead of decahedral quasicrystalline phase during the solidification process; the morphology of primary I-phase in the solidification microstructure changed from petal-like one (60-80 μm) to spherical one (≤15 μm). When the mass fraction of Ca reaches 0.05%, spherical I-phase with the largest quantity, highest spheroidization rate and highest circular degree can be obtained. Meanwhile, due to the changed morphology and the decreased size of primary I-phase, the hardness of Mg-Zn-Y-Ca master alloy is reduced. The application of spherical I-phase as particulate reinforced phase provides great opportunities for the improvement of strength and toughness of magnesium alloys.
其他文献
LiNi0.5Mn1.5O4 was prepared under different cooling conditions. The electrochemical properties of LiNi0.5Mn1.5O4 prepared under different cooling conditions wer
Combining with the technology of self-compacting concrete, self-stressing concrete and concrete-filled steel tube, we can get self-compacting and self-stressing
Plasma arc welding was used to join SiCp/Al composite with titanium as alloying filler material. Microstructure of the weld was characterized by an optical micr
Nanosized nickel oxide powders were prepared by thermal decomposition of the nickel citrate gel precursors. The thermal decomposition and powder materials deriv
Spherical Li(Ni1/3Mn1/3Co1/3)O2 was prepared via the homogenous precursors produced by solution spray-drying method. The precursors were sintered at different t
New layered perovskite compounds, AgxNa2-xLa2Ti3O10 (x=0.2, 0.3 and 0.5) were synthesized by an ion-exchange reaction of Na2La2Ti3O10 with AgNO3 solution and ch
Four types of steel sheets containing 0.04%, 0.09%, 0.14% and 0.36% Si, respectively, were electrodeposited with a nickel layer of 3 μm in thickness and then g
Stable binary single source precursors (SSP) for the deposition of thin films of ceramic semiconductors of composition SnO·GeO were synthesized by close circui
The amorphous Fe78Si9B13 ribbons were bend stress relaxed at various temperature well below the crystallization temperature (Tx) for different time. The effect
Using spark plasma sintering(SPS) technique, TiC particle reinforced γ-TiAl composites were prepared with varying weight fraction of TiC powders. The effects o