摘要：模具加工已经成为汽车行业发展的重要基础，模具质量直接影响着汽车成品的质量。模具的质量不仅表现在零件的制造质量上，也表现在后期的安装及调试质量中，目前，汽车行业模具加工还存在这种质量问题，主要表现就是模具的过载失效、磨损失效和疲劳失效，本文主要分析冷冲压模具加工过程中存在的问题以及质量控制的措施。
关键词：冷冲压模具加工；问题；质量控制措施
Abstract: mold processing has become an important base for the development of automotive industry, mould directly affects the quality of automobile product quality. Mold quality is not only reflected in the manufacturing quality of the parts, but also in the installation and commissioning quality, at present, processing industry mold car also has this kind of quality problems, mainly is the mold of overload failure, wear failure and fatigue failure, the paper mainly analysis of cold stamping die processing problems and measures quality control.
Keywords: cold stamping mould processing; problem; quality control measures
[中图分类号] TG385.2[文献标识码]A[文章编号]
近些年來，随着人们生活水平的提高，汽车的销量呈现出逐年增长的趋势，在汽车生产中，很多零部件需要历来模具的加工，模具加工已经成为汽车行业发展的重要基础，模具的加工和安装质量直接影响着汽车成品的质量。模具的质量不仅表现在零件的制造质量上，也表现在后期的安装及调试质量中。因此，在模具加工中，必须要采取必要的措施，制造质量和安装质量，避免安全事故的发生，保证汽车的整体质量。目前，在我国模具的加工工还存在各种问题，下面就对这些问题进行集中的探讨并提出相应的解决方式。
1、冷冲压模具安装过程中的问题
冷冲压模具的安装可以分为两个部分，一个部分就是将模具安装到模架上，另外一个部分就是将安装好的整套模具放入冲床内。
对于模具在模架中的安装，在安装之前要将模架的毛刺清理干净，在装配前检查所有的螺钉是否固定，是否符合标准规定的要求，对于带有导向装置的模架，在将其装进模具时一般不需要调整模板的位置，但是在装配的过程中，要对模板进行检查，看其中是否有脏物，如果有赃物要及时的清洁，防止造成不对中情况的产生。对于各个模板的组装，均要设置好定位销，保证安装的位置，在安装时要控制好定位销的深入，保证安装的有效性，如果发现销有磨损的情况，要及时更换。
在装配模具的过程中，要将装配好的模板与定位销对准，用工具进行敲打使两者可以平坦的结合在一起，在将紧固螺钉先用人工旋入，再利用扳手将其紧固，在拧螺钉要注意不能一步到位，要使用逐步到位的方式，保持安装的均衡性。在冲床的死点位置进行安装时，不能露出钢珠保持架的导套。在模具组装完成装入冲床时，根据实际的定位情况安装固定螺钉及定位销。在这两个过程中，很容易由于操作的失误出现质量问题，导致以下问题的产生：
1.1 过载失效
过载失效即材料的承载力难以抵抗工程过程中的的荷载引起的失效，这种失效包括韧度不足和强度不足。由于材料韧度发生的过载失效危害较大，这种失效常常是突发性的，容易导致人身事故的发生，给安全生产带来了较大的威胁，在这宗失效情况下模具很容易出现开裂、冲头断裂甚至爆裂的情况，难以修复。由于强度不足带来的失效在新模具中较为承建，这种失效与工作和在和模具的硬度有着密切的关系，一般情况下，冷挤冲头的硬度小于62HRC、黑色金属的冷镦冲头强度小于56HRC时容易出现强度过载失效，这说明材料的强度不足。一般解决这种失效的方法是变形失效增加硬度、脆断失效降低硬度。
1.2 磨损失效
磨损失效即模具被加工材料与工作部位之间产生的摩擦损耗，导致模具工作的刃口和冲头形状以及尺寸发生变化的失效情况，具体包括正常磨损和非正常磨损两种；正常磨损即模具的被加工材料与工作部位在工作时发生的正常损耗，飞正常损耗即在局部高压力作用下被加工材料与工作部位的咬合，从而导致被加工产品表面出现磨损、划痕等情况，一般这种情况容易出现在弯曲、拉伸的模具以及冷挤压模具中。
1.3 疲劳失效
由于冷冲压模具都是以一定的能量和速度作用周期施工，这与疲劳试验有着一些相似性，模具的断裂寿命也大多集中在1000到5000次，在长期的运行工作中，容易出现裂纹，一般模具的裂纹大多出现在材料的表面部位，如应力集中部位、晶界、碳化物部位，一旦裂纹产生，那么模具就是快速的产生失稳扩展，疲劳失效是模具加工中最为常见的问题。
2、冷冲压模具加工过程中的质量控制措施
为了控制以上问题的产生，可以采取改进现阶段的加工流程，按照以下两种工艺流程来进行：
2.1 工艺流程一
工艺流程是按照轧材毛坯下料（铸造连轧毛坯）、加热、锻造、进冷床水雾（进冷床水雾）、淬火冷却的流程进行，在淬火冷却的过程中，要将冷却的速度控制在20到45℃/min，将下贝氏体等温度控制在25min左右，空冷的温度为220到280℃，再进行地炕保温和回火，在回火操作中，要控制好回火的时间和温度，回火完成之后，再进行埋沙保温冷却。在整个工艺流程完成之后，对模具样品进行抽样检查，看样品的合格率，如果合格率不符合规定的标准要求，则在第一时间进行整改。
2.1 工艺流程二
另外一个工艺流程是按照金属模加压铸造、进冷床水雾（进冷床水雾）、淬火冷却的工艺进行，在淬火冷却的过程中，同样将温度保持在20到45℃/min，将下贝氏体等温度控制在25min左右，空冷的温度为220到280℃，在进行地坑保温和回火，回火的过程中也要控制要时间，最后进行埋沙保温冷却和抽样检查。
参考文献：
【1】于维民.冷冲压模具加工过程中的问题与质量控制[期刊论文]，应用能源技术，2009，07（25）
【2】陆茵.冷冲模具使用寿命的影响及对策[期刊论文]，金属加工(冷加工). 2008(12)
【3】周丹薇.冷冲压模具设计中合理工序安排与模具结构分析[期刊论文]，哈尔滨职业技术学院学报. 2007(02)
【4】林明山. 冷冲压模具的安装调整与故障排除技术[期刊论文]，模具制造. 2006(05)
关键词：冷冲压模具加工；问题；质量控制措施
Abstract: mold processing has become an important base for the development of automotive industry, mould directly affects the quality of automobile product quality. Mold quality is not only reflected in the manufacturing quality of the parts, but also in the installation and commissioning quality, at present, processing industry mold car also has this kind of quality problems, mainly is the mold of overload failure, wear failure and fatigue failure, the paper mainly analysis of cold stamping die processing problems and measures quality control.
Keywords: cold stamping mould processing; problem; quality control measures
[中图分类号] TG385.2[文献标识码]A[文章编号]
近些年來，随着人们生活水平的提高，汽车的销量呈现出逐年增长的趋势，在汽车生产中，很多零部件需要历来模具的加工，模具加工已经成为汽车行业发展的重要基础，模具的加工和安装质量直接影响着汽车成品的质量。模具的质量不仅表现在零件的制造质量上，也表现在后期的安装及调试质量中。因此，在模具加工中，必须要采取必要的措施，制造质量和安装质量，避免安全事故的发生，保证汽车的整体质量。目前，在我国模具的加工工还存在各种问题，下面就对这些问题进行集中的探讨并提出相应的解决方式。
1、冷冲压模具安装过程中的问题
冷冲压模具的安装可以分为两个部分，一个部分就是将模具安装到模架上，另外一个部分就是将安装好的整套模具放入冲床内。
对于模具在模架中的安装，在安装之前要将模架的毛刺清理干净，在装配前检查所有的螺钉是否固定，是否符合标准规定的要求，对于带有导向装置的模架，在将其装进模具时一般不需要调整模板的位置，但是在装配的过程中，要对模板进行检查，看其中是否有脏物，如果有赃物要及时的清洁，防止造成不对中情况的产生。对于各个模板的组装，均要设置好定位销，保证安装的位置，在安装时要控制好定位销的深入，保证安装的有效性，如果发现销有磨损的情况，要及时更换。
在装配模具的过程中，要将装配好的模板与定位销对准，用工具进行敲打使两者可以平坦的结合在一起，在将紧固螺钉先用人工旋入，再利用扳手将其紧固，在拧螺钉要注意不能一步到位，要使用逐步到位的方式，保持安装的均衡性。在冲床的死点位置进行安装时，不能露出钢珠保持架的导套。在模具组装完成装入冲床时，根据实际的定位情况安装固定螺钉及定位销。在这两个过程中，很容易由于操作的失误出现质量问题，导致以下问题的产生：
1.1 过载失效
过载失效即材料的承载力难以抵抗工程过程中的的荷载引起的失效，这种失效包括韧度不足和强度不足。由于材料韧度发生的过载失效危害较大，这种失效常常是突发性的，容易导致人身事故的发生，给安全生产带来了较大的威胁，在这宗失效情况下模具很容易出现开裂、冲头断裂甚至爆裂的情况，难以修复。由于强度不足带来的失效在新模具中较为承建，这种失效与工作和在和模具的硬度有着密切的关系，一般情况下，冷挤冲头的硬度小于62HRC、黑色金属的冷镦冲头强度小于56HRC时容易出现强度过载失效，这说明材料的强度不足。一般解决这种失效的方法是变形失效增加硬度、脆断失效降低硬度。
1.2 磨损失效
磨损失效即模具被加工材料与工作部位之间产生的摩擦损耗，导致模具工作的刃口和冲头形状以及尺寸发生变化的失效情况，具体包括正常磨损和非正常磨损两种；正常磨损即模具的被加工材料与工作部位在工作时发生的正常损耗，飞正常损耗即在局部高压力作用下被加工材料与工作部位的咬合，从而导致被加工产品表面出现磨损、划痕等情况，一般这种情况容易出现在弯曲、拉伸的模具以及冷挤压模具中。
1.3 疲劳失效
由于冷冲压模具都是以一定的能量和速度作用周期施工，这与疲劳试验有着一些相似性，模具的断裂寿命也大多集中在1000到5000次，在长期的运行工作中，容易出现裂纹，一般模具的裂纹大多出现在材料的表面部位，如应力集中部位、晶界、碳化物部位，一旦裂纹产生，那么模具就是快速的产生失稳扩展，疲劳失效是模具加工中最为常见的问题。
2、冷冲压模具加工过程中的质量控制措施
为了控制以上问题的产生，可以采取改进现阶段的加工流程，按照以下两种工艺流程来进行：
2.1 工艺流程一
工艺流程是按照轧材毛坯下料（铸造连轧毛坯）、加热、锻造、进冷床水雾（进冷床水雾）、淬火冷却的流程进行，在淬火冷却的过程中，要将冷却的速度控制在20到45℃/min，将下贝氏体等温度控制在25min左右，空冷的温度为220到280℃，再进行地炕保温和回火，在回火操作中，要控制好回火的时间和温度，回火完成之后，再进行埋沙保温冷却。在整个工艺流程完成之后，对模具样品进行抽样检查，看样品的合格率，如果合格率不符合规定的标准要求，则在第一时间进行整改。
2.1 工艺流程二
另外一个工艺流程是按照金属模加压铸造、进冷床水雾（进冷床水雾）、淬火冷却的工艺进行，在淬火冷却的过程中，同样将温度保持在20到45℃/min，将下贝氏体等温度控制在25min左右，空冷的温度为220到280℃，在进行地坑保温和回火，回火的过程中也要控制要时间，最后进行埋沙保温冷却和抽样检查。
参考文献：
【1】于维民.冷冲压模具加工过程中的问题与质量控制[期刊论文]，应用能源技术，2009，07（25）
【2】陆茵.冷冲模具使用寿命的影响及对策[期刊论文]，金属加工(冷加工). 2008(12)
【3】周丹薇.冷冲压模具设计中合理工序安排与模具结构分析[期刊论文]，哈尔滨职业技术学院学报. 2007(02)
【4】林明山. 冷冲压模具的安装调整与故障排除技术[期刊论文]，模具制造. 2006(05)