Composite coatings were obtained on A3 steel by hot dipping aluminum(HDA) at 720 ℃ for 6 min and micro-plasma oxidation(MPO) in alkali electrolyte. The surface
【机 构】
：
Department of Environment Science and Chemical Engineering,Institute of Mechanics,College of Materia
论文部分内容阅读
Composite coatings were obtained on A3 steel by hot dipping aluminum(HDA) at 720 ℃ for 6 min and micro-plasma oxidation(MPO) in alkali electrolyte. The surface morphology, element distribution and interface structure of composite coatings were studied by means of XRD, SEM and EDS. The results show that the composite coatings obtained through HDA/MPO on A3 steel consist of four layers. From the surface to the substrate, the layer is loose Al2O3 ceramic, compact Al2O3 ceramic, Al and FeAl intermetallic compound layer in turn. The adhesions among all the layers are strengthened because the ceramic layer formed at the Al surface originally, FeAl intermetallic compound layer and substrate are combined in metallurgical form through mutual diffusion during HDA process.Initial experiment results disclose that the anti-corrosion performance and wear resistance of composite coating are obviously improved through HDA/MPO treatment.
其他文献
Low-Co AB5-type Mm(NiCoMnA1)5Bx (x = 0, 0.1, 0.2 ) electrode alloys were prepared by casting and rapid quenching.The effects of the rapid quenching on the latti
A new concept of salt core, a melting temperature of which is lower than the solidus temperature of cast alloy,was introduced to produce an integrated casting p
In order to improve the in-flight characteristics of the atomizing droplets during high velocity wire arc spraying (HVAS), some changes have been operated on th
The content of zirconia has a remarkable influerce on transformation behavior and mechanical properties of Al2O3/ZrO2 (2Y) composites. When 15% and 20% ZrO2(2Y)
In the present work investigations have been made to see the role of metal oxides on the performance of the silver metal oxides electrical contact materials. Si
Recent research activities on the formation of micro-defects and porosity in organic coatings were reviewed. The mechanisms of aggressive ionic conduction throu
The oxidation of specimens with thermal barrier coating (TBC) consisted of nickel-base superalloy, low-pressure plasma sprayed Ni-28Cr-6Al-0.4Y (wt pct) bond co
The n-SiO2/Ni composite electro-brush plating coating was prepared on the 1045 steel substrate. SEM and TEM were utilized to analyze the surface and cross-secti
In research of YBCO coated conductors, the development of a oxide template for epitaxial growth of YBCO is very important. Matsumoto et al have demonstrated the
The influence of surface pre-treatments, shot-peening (SP) and laser remelting (LR), on oxygen permeation behaviors of titanium alloy TC11 was investigated. Opt